Using steel as raw material to produce the reducer, the part of the specifications of the reducer can also be used steel plate stamping forming technology is adopted to improve the production. Drawing die shapes used by reference to reducing tube surface size design, use after blanking punching die, stamping steel stretch forming.
The characteristics of stress distribution
(1) Under the action of the internal pressure, concentric reducer‘s size of terminal area pressure difference bending moments produced will cause to relatively open end, the small end of the relative shrinkage phenomenon.;
(2) the internal pressure under the action of eccentric reducer in central eccentric side inside the big end surface and eccentric side to the outer ring stress is the largest.
The use of eccentric reducer
When water absorption, water absorption section of the reduced pressure, gas will isolate was dissolved in the water, if the use is concentric reducer, these gases not discharge in time, will accumulate jams in the bumps, forming gas resistance. Pump will appear noise and carrying capacity drops greatly. If using eccentric reducer, isolate the gas discharge in time, will not form a vapor lock.
When reducing pipe diameter itself is not big, before and after the diameter difference is not big, with concentric reducer, possible gas resistance phenomenon is not so obvious, self-priming in the process of suction pressure change is not so big, so there was no harm.
Tuesday, January 4, 2022
Stamping forming and distribution characteristics of reducer
Related Posts:
Properties and classification of duplex stainless steelThe biphase in the name of the duplex stainless steel is mainly derived from the microstructure of the alloy. The duplex stainless steel usually conta… Read More
The effect of mechanical testing on stainless steel platesMechanical testing of stainless steel plates are used to generate data that can be used for design purposes or as part of the material connection proc… Read More
Creep reaction and test experiment of stainless steel plateCreep is a slow failure mechanism, which may occur when stainless steel plates are exposed to higher than the elastic limit for a long time. Creep is … Read More
Lamellar tearing defect of stainless steel plate in weldingStratified tears may sometimes occur in rolled steel plates with poor thickness ductility. The main characteristic of lamellar tear is that it appears… Read More
Test method and test error of Brinell and Vivtorinox hardness for stainless steel plate and other metalsBrinell test was designed by Swedish researchers in early twentieth Century. As shown in Fig. 1 (a), the test involves pressing the hardened steel bal… Read More
0 comments:
Post a Comment