When austenitic stainless steel tubes are heated or cooled through the temperature range 425-900C (800-1650F), chromium tends to combine with carbon to form chromium carbides. The carbides precipitate preferen- tially at grain boundaries depleting chromium from the adjacent areas. This reduces the corrosion resistance of the chromium depleted areas, sensitizing the alloy to Intergranular Attack (IGA).
The extent of carbide formation is dependent upon time at temperature and the carbon content of the alloy. Thus, exposure in the temperature range stated does not automatically mean that sensitization, or IGA will occur.

Sensitization may also result from slow cooling from solution annealing temperatures, or stress relieving – after welding – in the 425 to 900C (800 to 1650F) temperature range. In welded fabrications, sensitization and IGA may occur in corrosive environments in a rather narrow band on either side of or on the side opposite the weld, known as the heat affected zone (HAZ).

It is important to note that even if sensitization does occur, it is not of significant consequence unless the alloy is exposed to a corrosive environment. Sensitized stainless steel performs in a normal manner and safe manner in non-corrosive applications.

Order of Resistance

904L stainless steelHighest

This table lists some of the common stainless steels as to general resistance to pitting or crevice corrosion in aqueous environments where corrosive conditions may exist.

317L stainless steel 
329 stainless steel 
316/316L stainless steel 
304/304L stainless steel 
430 stainless steel 
410 stainless steel 
420 stainless steelLowest

Methods of Minimizing Intergranular Attack – IGA

1) Solution anneal above 1040C (1900F) followed by a rapid quench.

2) Use type 347 stainless steel, a Cb stabilized grade, or 321 stainless steel, a Ti stabilized grade.

3) Use a low carbon, 0.03% max. carbon steel grade such as 304L stainless steel, 316L stainless steel, 317L stainless steel or 904L stainless steel.

With today’s technology, carbon steel is economically reduced to very low residuals. The low carbon grades are the standard forwelded fabrication.

ASTM A262 practice A to E are standard tests to determine susceptibility to IGA. Practice E, the Huey test, is widely used.

Source: wilsonpipeline Pipe Industry Co., Limited (www.wilsonpipeline.com)

Related Posts:

  • How to process the inner thread of the stainless steel pipe fittingsWhether it is stainless steel welded pipe fittings or stainless steel seamless pipe fittings have internal thread, this kind of internal thread is how… Read More
  • Stainless Steel 90º ElbowStainless Steel 90º ElbowA stainless steel 90º elbow is a pipe fitting which you can used to change the flow direction in a stainless steel 90º elbow … Read More
  • Stainless Steel 180º ElbowStainless Steel 180º Elbowstainless steel 180º elbow is like 45º or 90º elbow, but the flow direction change is 180 degree. It looks like the flow flu… Read More
  • Reducing TeeA Reducing Tee is also called “unequal tee“, which means the tee branch pipe diameter is not same with the run pipe of the tee. Commonly, in a reducin… Read More
  • Straight TeesStraight TeesA Straight Tee means a tee of pipe fitting which the branch outlet has a 90 degree direction turning from the main pipe of the tee. Commo… Read More

0 comments:

Post a Comment