Hot rolled steel
Hot-rolled is with continuous casting slab or blooming slab as raw material, after reheating furnace heating, high pressure water descaling into roughing mill, roughing material by the cutting head, tail, and then enter the finishing mill, the implementation of a computer-controlled rolling made the final rolling after coiling after the laminar cooling (computer-controlled cooling rate) and the coiler, straight hair volume. Straight hair the volume of the head, the tail is often poor, was a tongue-and fishtail, thickness, width, precision the edge often there is a wave-shaped, folding, pyramid defects. Coil weight heavier coil diameter of 760mm. (Normal pipe industry prefer to use.) Straight hair volume by the cutting head, tail cutting, trimming, and multi-pass straightening flat finishing line treatment, a cutting board or heavy volume, that is, to become: hot-rolled steel plate, flat hot-rolled steel coils, slitting with other products. Serve hot finishing volume descaled, pickled and oiled hot-rolled pickled coils.
Cold formed steel
Cold formed is as raw material, after oxide removal by pickling tandem cold formed finished rolling hard roll, work hardening due to the volume of the rolling hard due to the continuous cold deformation strength, hardness rise, tough Plastic indicators declined, stamping performance will deteriorate, and can only be used for simple deformation of the parts. Rolling hard roll can be used as the raw material of the hot-dip galvanizing plant, hot dip galvanizing line set annealing line. Rolling hard roll weight is generally 6 to 13.5 tons, the coil diameter of 610mm. The general cold strip mills, volume should go through continuous annealing (CAPL unit) to eliminate cold hardening and rolling stress, or batch annealing reach the mechanical properties of the corresponding standard specifies. The cold-formed steel sheet surface quality, appearance, dimensional accuracy superior to the hot-rolled sheet, and right rolling thin product thickness to about 0.18mm.
Difference between hot rolled and cold formed steel:
1, cold formed steel to allow cross-section a local buckling, which can make full use of the rod buckling bearing capacity;-section hot rolled steel does not allow local buckling occurs.
2, the residual stress of the hot rolled steel and cold-formed steel produced by different reasons, so the distribution of the cross section is also very different. The residual stress distribution in the cross section of cold-formed steel bending, residual stress distribution in the hot rolling steel or welded steel cross-section is a film type.
3 free torsional stiffness of hot rolled steel, cold-formed steel, the torsional properties of hot-rolled steel is better than cold-formed steel.
Tuesday, January 4, 2022
Difference between hot rolled and cold formed steel
Related Posts:
Causes and preventive measures for pitting corrosion of stainless steel plateWhat is stainless steel pitting?To understand this concept, we must first understand the excellent corrosion resistance principle of stainless steel. … Read More
Analysis of the characteristics of third generation duplex stainless steelThe first generation of duplex stainless steel is 3re60 in the 1960s, which has the problem of welding thermal zone. The second generation was develop… Read More
The processing forms and difficulties of stainless steel pipe fittingsStainless steel pipe fittings are made of bending and deformation. In the process of processing, there will always be some difficult aspects of proces… Read More
Preparation of stainless steel bar before the surface pickling processAs a kind of steel widely used in Chinese life, stainless steel is highly adaptable and has high corrosion resistance. The main types of stainless ste… Read More
Characteristics and application of stainless steel seamless pipesStainless steel pipe can be pided into two kinds of stainless steel seamless pipe and stainless steel welded pipe. According to the shape of the secti… Read More
0 comments:
Post a Comment